High-Q-Bond SE
B.J.M. Laboratories Ltd. · Quelle
Product Description
Self-etch, self-adhesive dual-cure permanent resin cement
- A self-etch, self-adhesive dual-cure, radiopaque permanent resin cement that does not require etching, priming or bonding.
- ISO 4049 classification: Type 2, Class 3.
- Radiopacity value above 2.5mm Aluminium. (Radiopacity is defined as the ability of a material to be visible in x-ray photographs.)
- Forms ideal bond with metal alloys, porcelain, ceramic, dentin, enamel,
- Has a chemical affinity for metal.
- A dual-cure cement – it has a self curing mechanism which can also be light cured for an immediate set and extra strength at the margins.
- Light curing High-Q-Bond SE gives restorations immediate stability and easy clean up of excess material.
- Features high retention and total margin integrity.
- Administration via Automix syringe saves application time and guarantees consistent mix.
- Available in 3 shades: A2, White and Translucent. To see shade guide visit bjmlabs.com.
- Marketed since 2008 with no changes in formula. No complaints of any health-related or chemical performance issues were received.
Indications
- Permanent cementation of crowns and bridges, inlays and onlays, posts and cores, ceramic crowns, and Maryland bridges
- Metal alloys adhesive opaquer
- Porcelain repair
- Proven Color Stability over time
Technical Data
Compressive strength: > 150 MPa
Flexural strength: > 100 MPa
Water sorption: ≤ 40 μg/mm3
Solubility: ≤ 7.5 μg/mm3
Shear bond strength to etched enamel: > 10 MPa
Shear bond strength to un-etched dentin: > 5 MPa
Shear bond strength to pretreated metal alloy: > 10 MPa
Shear bond strength to pretreated porcelain / ceramic surface (Zirconia): > 5 MPa
Film thickness: >50
Radiopacity: >100 % Al
Working time (in ambient light and temperature): > 90 seconds, in the 1.5 - 3.5 min interval
Setting time (in oral temperature): < 10 minutes, in the 2.5 - 4.5 min interval
Light curing time: 10 – 20 seconds
Compatible with LED: Yes
Compatible with halogen light: Yes
Compatible with Plasma ark light lamp: Yes
Shelf life: 2 Years
Produktinformationen
| Hersteller | B.J.M. Laboratories Ltd. |
|---|---|
| Material | Self-etch, self-adhesive dual-cure permanent resin cement |
| Shelf Life | 2 Years |
| Solubility | ≤ 7.5 μg/mm3 |
| Anwendung | Permanent cementation of crowns and bridges, inlays and onlays, posts and cores, ceramic crowns, and Maryland bridges |
| Röntgenopazität | >100 % Al |
| Setting Time | < 10 minutes |
| Working Time | > 90 seconds |
| Film Thickness | >50 |
| Led Compatible | Ja |
| Water Sorption | ≤ 40 μg/mm3 |
| Delivery Format | Automix Syringe |
| Available Shades | A2, White, Translucent |
| Biegefestigkeit | > 100 MPa |
| Light Curing Time | 10 – 20 seconds |
| Iso Classification | Type 2, Class 3 |
| Druckfestigkeit | > 150 MPa |
| Halogen Light Compatible | Ja |
| Plasma Arc Light Compatible | Ja |
| Shear Bond Strength (metal Alloy) | > 10 MPa |
| Shear Bond Strength (etched Enamel) | > 10 MPa |
| Shear Bond Strength (un Etched Dentin) | > 5 MPa |
| Shear Bond Strength (porcelain/ceramic) | > 5 MPa |