Kera S-Powder CoCr
DENTAS d.o.o. · Quelle
CoCrW-Powder for additive manufacturing of dental restorations for the laser-melting process, Type 5.
Clinical proven composition on the base of Kera®-Disc
Excellent material properties for many indications
Approved for the most common 3D-Laser-Melting Systems
Suitable for all high fusing veneering ceramics
Indications:
- Crowns and bridges
- Partial dentures
- Implant supported restorations
- Secondary and Tertiary frames
Technical data:
- Yield strength RP 0.2%: 770 MPa
- Percentage elongation at break: 8%
- Modulus of elasticity: 200 GPa
- Tensile strength: 1021 MPa
- Density: 855g/cm3
- Corrosion resistance: < 200 my/cm3
- WAK (25-500°C): 14.2 x 10-6K-1
- Hardness (HV 10/30): 352
- Composition: Co 61.65. Cr 27.75. W8.45. Si 1.61. Mn < 1%. Fe < 1%. Other < 0.1%
Produktinformationen
| Hersteller | DENTAS d.o.o. |
|---|---|
| Typ | Type 5 |
| Density | 855 g/cm³ |
| Process | Laser-melting process |
| Anwendung | Additive manufacturing of dental restorations |
| Zusammensetzung | Co 61.65, Cr 27.75, W 8.45, Si 1.61, Mn < 1%, Fe < 1%, Other < 0.1% |
| Materialtyp | CoCrW-Powder |
| Wak 25 500°c | 14.2 x 10-6K-1 |
| Tensile Strength | 1021 MPa |
| Hardness Hv 10/30 | 352 |
| Corrosion Resistance | < 200 my/cm³ |
| Modulus Of Elasticity | 200 GPa |
| Yield Strength Rp 0.2% | 770 MPa |
| Percentage Elongation At Break | 8% |