priti multidisc ZrO2 Multi Translucent (5Y/3Y-TZP)
Pritidenta GmbH
Multilayer zirconia disc combining advantages of 3Y (Translucent with very high strength) and 5Y (High Translucent with optimum translucency) in one blank. Features good cervical opaque masking properties, gradual transition into the dentine, and increasing translucency in the transition to the incisal area of > 800 MPa in all layers. Suitable for all indications including highly aesthetic monolithic, fully anatomical crowns, partial crowns, bridges with up to 14 units, inlays, onlays, veneers, abutments, and frameworks. Compatible with staining, cutback, and veneering techniques.
Produktinformationen
| Hersteller | Pritidenta GmbH |
|---|---|
| Cte | (10.5 +/- 0.5) x 10^-6 K^-1 |
| Heights | 16 mm, 20 mm, 25 mm |
| Material | Zirconium dioxide Type II, Class 5 according to DIN EN ISO 6872 |
| Sintering | Rapid sintering approx. 4 hours, approved for restorations with up to 3 units |
| Indikation | Crowns, partial crowns, bridges up to 14 units, inlays, onlays, veneers, abutments, frameworks |
| Zusammensetzung | 5Y-TZP upper layer (3 mm), 5Y- and 3Y-TZP middle layer (5 mm), 3Y-TZP lower layer (12 mm) |
| Blank Diameter | 98.5 mm |
| Available Shades | All 16 VITA classic shades + 3 Bleach shades |
| Biegefestigkeit | typical mean value >= 1,100 MPa |
| Translucency Gradient | > 40% to > 49% |
| Lower Layer Translucency | > 40% (3Y-TZP, > 1,150 MPa) |
| Upper Layer Translucency | > 49% (5Y-TZP, > 800 MPa) |