SHT-C ZIRCONIA DISK
Santa Barbara SRL · #29056 · Quelle
Santa Barbara DentalSanta Barbara Super High Translucent Color ZirconiaCompatible with the entire Santa Barbara Dental fleet •5 Colors • Flexural Strength 900Mpa • Translucency 45% • Natural tooth looking • Lightweight and durable • Biocompatible • Low thermal conductivity • Suitable for crowns and anterior bridges Chemical Composition
Components
ZrO2+HfO2+Y2O3 ≥99%
Y2O3 7.0%-7.8%
Al2O3 <0.15%
Other Oxides <0.5%
Physical Properties
Properties
Density before sintering (g·cm−3) 3.15 ±0.05
Density after sintering (g·cm−3) 6.08 ±0.01
CTE (25-500°C) 10.5 ±0.05
Flexural strength after sintering (Mpa) 900
Aging surface monoclinic phase content <15%
Light Transmittance <45%
Chemical solubility after sintering (µg·cm−2) <100
Cytotoxicity Livello 0
Radioactivity (Bq·g−1) <0.1
Sintering Temperature (recommended 1530) 1500 -1550
Produktinformationen
| Hersteller | Santa Barbara SRL |
|---|---|
| Farbe | 5 |
| Transluzenz | 45% |
| Colore Cialda | A1, A2, A3, B1, B2 |
| Misure Cialde | ∅98×10, ∅98×12, ∅98×14, ∅98×16, ∅98×18, ∅98×20, ∅98×25, ∅98×22 |
| Biegefestigkeit | 900 Mpa |