Vitra 413
DWS srl · Quelle
Vitra 413
Opaline transparency, smooth surfaces, white translucence.
VITRA 413 is a photosensitive material to be used with DWS stereolithographic 3D printers, developed for high-definition prototypes and concept-design.
VITRA 413 is suitable for the production of both thin and thick models. It is the ideal material for obtaining smooth and precise transparent-opaline samples.
Treatments are required to counteract yellowing.
Industries
Educational Eyewear Fashion & accessories Footwear General manufacturing
Areas of Applications
Mechanics and parts Prototyping
Vitra 413 main features
- Smooth Surfaces
- Transparent
- High resolution and precision
- High accuracy
Technical data
Technical characteristics of the liquid material
Environmental Values for Use: 22°C - 27°C - max, RH 40% - 60%
Appearance / Colour: Liquid / Light Yellow
Density: 1,05 g/cm³
Viscosity: 600 ~ 900 mPa•s at 25°C
Technical characteristics of the resin after UV curing
Elongation at Break (%): 2 ~ 3
Shore Hardness (Shore A)
Shore Hardness (Shore D): 86 ~ 88
Flexural Strength (MPa): 60 ~ 115
Flexural Modulus (MPa): 1750 ~ 2650
Tensile Strength (MPa): 20 ~ 40
Tensile Modulus (MPa): 1500 ~ 2250
HDT@0,46MPa: 54 ~ 58
HDT@1,81MPa
Notched IZOD (J/m)
H2O absorption in 24h (%)
Application / Use: Transparent Prototypes, Clear Functional Parts
Produktinformationen
| Hersteller | DWS srl |
|---|---|
| Density | 1.05 g/cm³ |
| Viskosität | 600 ~ 900 mPa•s at 25°C |
| Appearance | Liquid / Light Yellow |
| Industries | Educational, Eyewear, Fashion & accessories, Footwear, General manufacturing |
| Anwendung | Transparent Prototypes, Clear Functional Parts |
| Hdt@0.46mpa | 54 ~ 58 °C |
| Tensile Modulus | 1500 ~ 2250 MPa |
| Flexural Modulus | 1750 ~ 2650 MPa |
| Tensile Strength | 20 ~ 40 MPa |
| Biegefestigkeit | 60 ~ 115 MPa |
| Elongation At Break | 2 ~ 3 % |
| Areas Of Applications | Mechanics and parts, Prototyping |
| Shore Hardness (shore D) | 86 ~ 88 |
| Environmental Values For Use | 22°C - 27°C, RH 40% - 60% |