Bright Temporary C&B
DMP Dental Industry S.A. · source
Bright Temporary C&B is a self-curing, moldable composite designated for the construction of temporary crown and bridge restorations, available in three different ratios (1:1, 4:1, 10:1). It offers an excellent aesthetic result and in combination with its optimal mechanical properties is an ideal tool for fabricating provisional restorations. It produces low temperatures during intra-oral setting which protect against damage to the dental pulp.
Indications
- Temporary crowns and bridges
- Temporary inlays and onlays
Characteristics - Advantages
- Superior aesthetics
- Minimal increase in temperature during polymerization
- Precise and easy fit of the temporary crown / bridge due to low shrinkage
- Optimum elastic phase
- Long lasting and durable
- Extremely high polishability
Technical Data
| Specification | 1:1 | 4:1 | 10:1 |
|---|---|---|---|
| Mixing ratio (base:catalyst) | 1:1 | 4:1 | 10:1 |
| Working time (min) | 0:40-1:00 | 0:40-1:00 | 0:40-1:00 |
| Curing time in mouth (min) | 1:00-2:30 | 1:00-2:30 | 1:00-2:30 |
| Flexural strength (MPa) | 91 | 89 | 92 |
| Compressive strength (MPa) | 295 | 288 | 291 |
| Max. polymerization temperature (oC) | <40 | <40 | <40 |
Product Information
| Manufacturer | DMP Dental Industry S.A. |
|---|---|
| Type | Self-curing moldable composite |
| Application | Temporary crown and bridge restorations |
| Available Shades | 01 (A1), 02 (A2), 03 (A3), 07 (B1), 25 (Bleach) |
| Working Time Min | 0:40-1:00 |
| Mixing Ratio Options | 1:1, 4:1, 10:1 |
| Curing Time In Mouth Min | 1:00-2:30 |
| Flexural Strength Mpa 1 1 | 91 |
| Flexural Strength Mpa 4 1 | 89 |
| Flexural Strength Mpa 10 1 | 92 |
| Compressive Strength Mpa 1 1 | 295 |
| Compressive Strength Mpa 4 1 | 288 |
| Compressive Strength Mpa 10 1 | 291 |
| Max Polymerization Temperature Oc | <40 |