Glazic Lithium Disilicate Glass Ceramic
Besmile Biotechnology Co,. Ltd · source
Product Introduction
Glazic is a zirconia-reinforced lithium disilicate glass ceramic made from nano-grade, high-quality raw materials, resulting in a fine-grained microstructure that offers outstanding machinability and consistently stable aesthetic results. With its excellent mechanical strength, natural shade matching, and lifelike fluorescence and opalescence, Glazic ensures both durability and beauty. Its simple processing and minimally invasive properties make it an ideal all-ceramic material for efficient chairside aesthetic restorations such as crowns, veneers, inlays, and onlays.
Advantages
Super Strength
Ultra fine-grained microstructure with completely dissolved zirconia in glass. Flexural Strength (3-point) ≥ 400 MPa (up to 3-unit anterior bridge)
Lifelike Aesthetics
Outstanding translucency from proper light scattering Lifelike opalescence with natural fluorescence Personalized aethetics with varied shades available
Simple Processing
Ideal material for CAD/CAM processing with super strength Lower chipping occurrence with high edge stability Proper hardness and flexural strength(uncrystallized) guarantee milling burs long lifespan
Super Minimally Invasive
Ultra-thin veneer to 0.3mm Maximum preservation of natural tooth structure Long-term management to maintain endodontic health
Material Properties
- Composition: SiO2, Al2O3, Li2O, Na2O, ZrO2, other oxides etc.
- Density [g/cm³]: ≥2.2
- Vickers hardness [HV10]: 480-520 (Crystallized)
- Biaxial flexural strength [MPa]: ≥400
- Fracture toughness [MPa·m^1/2]: >2.5
- Chemical solubility [µg/cm²]: <100
- CTE (500℃) [10^-6 K]: 9.7±0.5
- Crystallization Temp. [℃]: 840
Product Information
| Manufacturer | Besmile Biotechnology Co,. Ltd |
|---|---|
| Density | ≥2.2 g/cm³ |
| Composition | SiO2, Al2O3, Li2O, Na2O, ZrO2, other oxides etc. |
| Cte (500℃) | 9.7±0.5 10^-6 K |
| Vickers Hardness | 480-520 HV10 (Crystallized) |
| Application Areas | Crowns, veneers, inlays, onlays |
| Fracture Toughness | >2.5 MPa·m^1/2 |
| Chemical Solubility | <100 µg/cm² |
| Biaxial Flexural Strength | ≥400 MPa |
| Crystallization Temperature | 840 ℃ |
| Flexural Strength (3 Point) | ≥ 400 MPa (up to 3-unit anterior bridge) |