High-Q-Bond
B.J.M. Laboratories Ltd. · source
High-Q-Bond
Dual-cure permanent adhesive resin cement
Applications
- Final permanent cementation of crowns and bridges, inlays and onlays, posts and cores, ceramic crowns, and Maryland bridges
- Metal alloys adhesive opaque Porcelain repair
- Proven Color Stability over time
Product Description
- A multi-purpose, dual-cure, radiopaque, permanent adhesive resin cement.
- ISO 4049 classification: Type 2, Class 3.
- Radiopacity value above 2.5mm Aluminium. (Radiopacity is defined as the ability of a material to be visible in x-ray photographs.)
- Forms ideal bond with metal alloys, porcelain, ceramic, dentin, enamel.
- Has a chemical affinity for metal.
- A dual-cure cement – it has a self curing mechanism which can also be light cured for an immediate set and extra strength at the margins.
- Light curing High-Q-Bond gives your restorations immediate stability and easy clean up of excess material.
- Features high retention and total margin integrity.
- Marketed since 2000 with no changes in formula. No complaints of any health-related or chemical performance issues were received.
Technical Data
- Compressive strength: > 150 MPa
- Flexural strength: > 100 MPa
- Hardness by Shore A: ~80
- Water sorption: ≤ 40 μg/mm3
- Solubility: ≤ 7.5 μg/mm3
- Shear bond strength to etched enamel: > 10 MPa
- Shear bond strength to etched dentin: > 5 MPa
- Shear bond strength to metal alloy: > 10 MPa
- Shear bond strength to pretreated porcelain / ceramic surface (Zirconia): > 5 MPa
- Film thickness: >50
- Radiopacity: >100 % Al
- Working time (in ambient light and temperature): > 90 seconds, in the 1.5 - 3.5 min interval
- Setting time (in oral temperature): < 10 minutes, in the 2.5 - 4.5 min interval
- Light curing time: 10 – 20 seconds
- Compatible with LED: Yes
- Compatible with halogen light: Yes
- Compatible with Plasma ark light lamp: Yes
- Shelf life: 2 Years
Product Information
| Manufacturer | B.J.M. Laboratories Ltd. |
|---|---|
| Type | Dual-cure permanent adhesive resin cement |
| Shelf Life | 2 Years |
| Solubility | ≤ 7.5 μg/mm3 |
| Radiopacity | >100 % Al |
| Setting Time | < 10 minutes (2.5 - 4.5 min interval) |
| Working Time | > 90 seconds (1.5 - 3.5 min interval) |
| Film Thickness | >50 |
| Led Compatible | Yes |
| Water Sorption | ≤ 40 μg/mm3 |
| Curing Mechanism | dual-cure with self curing and light curing options |
| Flexural strength | > 100 MPa |
| Light Curing Time | 10 – 20 seconds |
| Radiopacity Value | above 2.5mm Aluminium |
| Bonding Substrates | metal alloys, porcelain, ceramic, dentin, enamel |
| Hardness By Shore A | ~80 |
| Compressive strength | > 150 MPa |
| Iso 4049 Classification | Type 2, Class 3 |
| Halogen Light Compatible | Yes |
| Plasma Ark Light Lamp Compatible | Yes |
| Shear Bond Strength To Metal Alloy | > 10 MPa |
| Shear Bond Strength To Etched Dentin | > 5 MPa |
| Shear Bond Strength To Etched Enamel | > 10 MPa |
| Shear Bond Strength To Pretreated Porcelain/ceramic | > 5 MPa |