Bright Light
DMP Dental Industry S.A. · #110110201 · source
Description
Bright Light is a versatile microhybrid light curing composite for both anterior and posterior restorations. Its great handling characteristics guarantee ease of application while its high gloss polishability increases the resistance against plaque. High filler loading results in excellent physical properties such as high diametral and flexural strength. Due to its very low water sorption it exhibits long lasting colour stability while maintaining its physical properties over a long period of time.
Indications
Anterior and posterior restorations
Class I - V restorations
Veneering of discoloured anterior teeth
Repair of composite and ceramic veneers
Splinting of mobile teeth
Characteristics - Advantages
- Great handling characteristics
- Very good marginal adaptation
- Very high fracture toughness
- High resistance to wear
- High polishability due to fine particles
- High aesthetic result-chameleon effect
- Strongly radiopaque
- Non-sticky
Technical Data
| Property | Value |
|---|---|
| Filled by weight (%) | 81 |
| Average filler particle size (μm) | 0.9 |
| Flexural Strength (MPa) | 130 |
| Polymerization shrinkage (%) | 2.0 |
| Water sorption (μg/mm3) | 10.5 |
| Compressive strength (MPa) | 300 |
| Radiopacity (mm of Al) | ≥1 |
Available Shades
- 01 - A1
- 02 - A2
- 03 - A3
- 05 - A3.5
- 06 - A4
- 07 - B1
- 08 - B2
- 09 - B3
- 12 - C2
- 13 - C3
- 16 - D3
- 04 - Opaque A2
- 19 - Incisal
- 24 - Bleach Extra
- 25 - Bleach
Informations produit
| Fabricant | DMP Dental Industry S.A. |
|---|---|
| Type | Microhybrid light curing composite |
| Application | Restaurations antérieures et postérieures |
| Radio-opacité | ≥1 mm of Al |
| Water Sorption | 10.5 μg/mm3 |
| Filled By Weight | 81% |
| Résistance à la flexion | 130 MPa |
| Résistance à la compression | 300 MPa |
| Polymerization Shrinkage | 2.0% |
| Average Filler Particle Size | 0.9 μm |