Cem-Implant
B.J.M. Laboratories Ltd. · source
Cem-Implant
Non-eugenol, self-cure resin cement for implants retained crowns
- A non-eugenol, acrylic-urethane polymer based temporary cement for implant luting.
- Long-term cementation for permanent implant retained restorations and long-term provisional.
Properties
- Self-cure cement.
- ISO 4049 Classification: Type 2, Class 1.
- Rigid final set that ensures marginal seal and firm retention.
- Available in 2 shades: gingival and white. To see shade guide visit bjmlabs.com.
- Marketed since 2004 with no changes in formula. No complaints of any health-related or chemical performance issues were received.
Technical Data
Flexural strength: ≥5 MPa, in the 8 – 19 MPa interval
Film thickness: ≤50 μm
Solubility: ≤7.5 μg/mm3
Water sorption: ≤40 μg/mm3
Linear shrinkage: <3%
Working time (in ambient light and temperature): > 90 seconds, in the 1.5 – 5.0 min interval
Setting time (in oral temperature): < 10 minutes, in the 2.5 – 6.0 min interval
Radiopacity: >100 Al%
Shelf Life: 2 Years
Informations produit
| Fabricant | B.J.M. Laboratories Ltd. |
|---|---|
| Type | Non-eugenol, acrylic-urethane polymer based temporary cement for implant luting |
| Shelf Life | 2 Years |
| Solubility | ≤7.5 μg/mm³ |
| Radio-opacité | >100 Al% |
| Film Thickness | ≤50 μm |
| Water Sorption | ≤40 μg/mm³ |
| Available Shades | Gingival and white |
| Linear Shrinkage | <3% |
| Self Cure Cement | Oui |
| Résistance à la flexion | ≥5 MPa, in the 8 – 19 MPa interval |
| Iso 4049 Classification | Type 2, Class 1 |
| Setting Time (in Oral Temperature) | < 10 minutes, in the 2.5 – 6.0 min interval |
| Working Time (in Ambient Light And Temperature) | > 90 seconds, in the 1.5 – 5.0 min interval |