DUTC - Disc ultra-translucent colored
Dentaco · source
Zirconium milling blanks with a diameter of 98 mm in a variety of thicknesses between 10 and 25 mm in a variety of colors
Technische Daten:
- Translucency (%): 42
- Flexural strength (MPa): 1200
- Material classification: 3 mol%
- Zirconium oxide, yttrium oxide stabilized
- Chem. composition: ZrO2+HfO2+Y203 ≥99%, Y203<6%
- Classification according to ISO 6872: Type II, Class 6
- Flexural strength / crack toughness MPa*m1/2: >6
- Thermal expansion coefficient 10-6 K-1g: 10,5
- Modulus of elasticity (GPa): >200
- Density in sintered condition (g/cm3): >6
Indikationen:
- Fully anatomical crown
- Bridge (max. 16 unit bridge, the absence of neighboring teeth may be 3 units in the anterior and 2 units in the posterior region)
- Inlay
- Veneer
- Partially or completely veneered ceramic crown and bridge
- Telescopic crown and custom abutment
Verfügbare Größen:
Available in different colors in the following sizes: 10, 12, 14, 16, 18, 20, 22 and 25 mm thickness
Informations produit
| Fabricant | Dentaco |
|---|---|
| Diamètre | 98 mm |
| Matériau | Zirconium oxide, yttrium oxide stabilized |
| Quantité | 3 |
| Translucidité | 42% |
| Crack Toughness | >6 MPa*m1/2 |
| Thickness Range | 10-25 mm |
| Résistance à la flexion | 1200 MPa |
| Density (sintered) | >6 g/cm3 |
| Chemical Composition | ZrO2+HfO2+Y203 ≥99%, Y203<6% |
| Available Thicknesses | 10, 12, 14, 16, 18, 20, 22, 25 mm |
| Modulus Of Elasticity | >200 GPa |
| Iso 6872 Classification | Type II, Class 6 |
| Material Classification | 3 mol% |
| Thermal Expansion Coefficient | 10,5 × 10-6 K-1 |