HT PLUS WHITE ZIRCONIUM
Santa Barbara SRL · #26838 · source
Santa Barbara DentalZIRCONIUM HT PLUS WHITEis the high-strength, high-translucency monolayer solution for excellent natural-looking results. It is supplied in white and can be colored as required, providing a variety of operative solutions. The high flexural strength (1350 MPa) enables safe and durable restorations suitable for all types of processing. Compatible with the entire Santa Barbara Dental fleet • Color: White • Flexural Strength 1350Mpa • Translucency 37% • Natural tooth looking • Lightweight and durable • Biocompatible • Low thermal conductivity • Suitable for crowns, bridges and veneers Chemical composition
Components
ZrO2+HfO2+Y2O3 ≥99%
Y2O3 4.5%-6.0%
Al2O3 <0.25%
Other oxides <0.15%
Physical Properties
Properties
Density before sintering (g cm−3) 3.15 ±0.05
Density after sintering (g cm−3) 6.09 ±0.01
CTE (25-500°C) 10.5 ±0.05
Flexural strength after sintering (Mpa) 1350
Aging surface monoclinic phase content <15%
Light Transmittance 37%
Chemical solubility after sintering (µg cm−2) <100
Cytotoxicity Level 0
Radioactivity (Bq g−1) <0.1
Sintering temperature 1500 -1550
Informations produit
| Fabricant | Santa Barbara SRL |
|---|---|
| Y2o3 | 4.5%-6.0% |
| Al2o3 | <0.25% |
| Couleur | Blanc |
| Poids | 480 g |
| Cytotoxicity | Level 0 |
| Other Oxides | <0.15% |
| Convient pour | crowns, bridges and veneers |
| Translucidité | 37% |
| Colore Cialda | A1, A2, A3, A3,5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4 |
| Misure Cialde | ∅98×10, ∅98×12, ∅98×14, ∅98×16, ∅98×18, ∅98×20, ∅98×25, ∅98×22 |
| Radioactivity | <0.1 Bq g−1 |
| Zro2+hfo2+y2o3 | ≥99% |
| Cte (25 500°c) | 10.5 ±0.05 |
| Résistance à la flexion | 1350 MPa |
| Light Transmittance | 37% |
| Sintering Temperature | 1500 -1550 |
| Density After Sintering | 6.09 ±0.01 g cm−3 |
| Density Before Sintering | 3.15 ±0.05 g cm−3 |
| Chemical Solubility After Sintering | <100 µg cm−2 |
| Aging Surface Monoclinic Phase Content | <15% |