MoguCera C Disc

CoCrMo milling disc with excellent properties for the manufacture of crowns, bridges, frameworks, telescopes, bars, attachments and implant supported superstructures. MoguCera C Disc is based on a non-precious ceramic alloy already used in the conventional casting technology. Free of nickel, beryllium, lead und cadmium. Type 4 pursuant to DIN EN ISO 22674 with a very wide range of indications.

Advantages for users:

• Medium hardness of 288 HV 10
• Excellent metal-ceramic Bonding
• Biocompatible
• Easy to work with and very to polish
• Laser weldable
• Suitable for dry and wet milling

Composition in percent by mass:

• Co: 65%
• Cr: 28%
• Mo: 5%
• C,Si,Nb,Mn,Fe: <1%

Technical properties:

• Proof stress (Rp 0.2): 413 MPa
• Ultimate tensile strength: 597 MPa
• Elongation: 12%
• Elastic modulus: 206 GPa
• Vickers hardness: 288 HV10
• Density: 8.3 g/cm³
• CTE (20-500°C): 14.5 x 10⁻⁶K⁻¹
• CTE (20-600°C): 14.8 x 10⁻⁶K⁻¹
• Laser weldable: Yes
• Type (DIN EN ISO 22674): 4