priti® multidisc ZrO₂ Multi Translucent
Pritidenta GmbH
High-performance zirconium dioxide disc offering outstanding strength with its special layering concept, which also achieves better masking of underlying teeth. Translucency from >49% to >40%. Three-layer structure: Upper layer 5Y-TZP >49% T. (3 mm) >800 MPa, Interlayer 3Y- & 5Y-TZP (5 mm), Lower layer 3Y-TZP >40% (Remaining height 12 mm) >1,150 MPa. Flexural strength: typical mean value >1,100 MPa. Homogeneous coloring. Consistently reproducible shades. Rapid sintering with a total time of approx 4 hours; approved for restorations with up to 3 units.
Informations produit
| Fabricant | Pritidenta GmbH |
|---|---|
| Type | Multi Translucent (MT) |
| Teintes | 16 VITA classical shades + 3 bleach shades |
| Matériau | Zirconium Dioxide (ZrO₂) |
| Indication | Single crowns, inlays, onlays, bridges up to 14 units, fully anatomical crowns and bridges, primary telescope parts, implant-supported superstructures up to 14 units, cut-back possible, good coverage of discolored teeth |
| Composition | 5Y-TZP / 3Y-TZP multilayer |
| Translucidité | >49% to >40% |
| Disc Diameter | 98.5 mm |
| Rapid Sintering | Approx 4 hours total time, up to 3 units |
| Available Heights | 16, 20, 25 mm |
| Résistance à la flexion | >1,100 MPa (typical mean) |