ProGlass Plus Cem
Silmet Ltd. · #17P9UN-C · source
Self-Adhesive Resin Modified Glass Ionomer Cement
ProGlass Plus Cem is a self-etching dual cure permanent cementation solution resin modified luting cement that is ideal for everyday cementation use.
Formulated to deliver excellent handling properties and easy cleanup with tack cure capabilities ProGlass Plus Cem delivers outstanding bond strength to tooth structures and common substrates—significantly higher than with other RMGI products.
Features
• Used in self-cure, light-cure, or dual-cure modes.
• No pretreatment required.
• Light cure option and rubbery consistency that allow easy removal of excess and shortens cleanup to seconds.
• Releases substantially higher fluoride to assist with remineralization of the natural dentition.
• No post-operative sensitivity.
• Moisture tolerant solution, when a dry field cannot be assured.
• Radiopaque and allows for useful diagnostic and excellent identification under x-ray.
• Does not require refrigeration.
• Low film thickness.
Properties
Compressive Strength 270 MPa
Flexural Strength 135 MPa
Compatible with halogen light Yes
Compatible with Plasma ark light lamp Yes
Compatible with LED Yes
Shear bond strength
- Composite -dentin 12 MPa
- Composite -enamel 19 MPa
- Glass Ceramic - lithium disilicate 6 MPa
- Ceramic Aluminim oxide 8 MPa
- Metal 13 MPa
- Zirconia 9 MPa
Film Thickness 10μm
Working Time 3 min ± 30 secs
Setting Time ≤ 5 min
Average inorganic filler (by weight) 65 wt%
Informations produit
| Fabricant | Silmet Ltd. |
|---|---|
| Type | Self-Adhesive Resin Modified Glass Ionomer Cement |
| Teinte | Universal (UN) |
| Cure Modes | Self-cure, light-cure, or dual-cure |
| Setting Time | ≤ 5 min |
| Working Time | 3 min ± 30 secs |
| Film Thickness | 10μm |
| Résistance à la flexion | 135 MPa |
| Compatible With Led | Oui |
| Résistance à la compression | 270 MPa |
| Compatible With Halogen Light | Oui |
| Average Inorganic Filler (by Weight) | 65 wt% |
| Compatible With Plasma Ark Light Lamp | Oui |