SHT ZIRCONIA
Santa Barbara SRL · #28783 · source
Santa Barbara DentalSuper-High Translucent ZirconiaCompatible with the entire Santa Barbara Dental fleet • Color: White • Flexural Strength 1000Mpa • Translucency 46% • Natural tooth looking • Lightweight and durable • Biocompatible • Low thermal conductivity • Suitable for anterior bridges Chemical Composition
Components
ZrO2+HfO2+Y2O3 ≥99%
Y2O3 7.0%-7.8%
Al2O3 <0.15%
Altri ossidi <0.15%
Physical Properties
Properties
Density before sintering (g·cm−3) 3.15 ±0.05
Density after sintering (g·cm−3) 6.08 ±0.01
CTE (25-500°C) 10.5 ±0.05
Flexural strength after sintering (Mpa) 1200 1000
Aging surface monoclinic phase content <15%
Light Transmittance <46%
Chemical solubility after sintering (µg·cm−2) <100
Cytotoxicity Livello 0
Radioactivity (Bq·g−1) <0.1
Sintering Temperature (recommended 1530) 1500 -1550
Informations produit
| Fabricant | Santa Barbara SRL |
|---|---|
| Couleur | Blanc |
| Poids | Lightweight and durable |
| Appearance | Natural tooth looking |
| Application | Suitable for anterior bridges |
| Cytotoxicity | Livello 0 |
| Translucidité | 46% |
| Radioactivity | <0.1 Bq·g−1 |
| Cte (25 500°c) | 10.5 ±0.05 |
| Biocompatibility | Biocompatible |
| Résistance à la flexion | 1000 Mpa |
| Light Transmittance | <46% |
| Thermal Conductivity | Low thermal conductivity |
| Sintering Temperature | 1500-1550°C (recommended 1530) |
| Density After Sintering | 6.08 ±0.01 g·cm−3 |
| Density Before Sintering | 3.15 ±0.05 g·cm−3 |
| Chemical Composition Y2o3 | 7.0%-7.8% |
| Chemical Composition Al2o3 | <0.15% |
| Flexural Strength After Sintering | 1000-1200 Mpa |
| Chemical Composition Altri Ossidi | <0.15% |
| Chemical Solubility After Sintering | <100 µg·cm−2 |
| Chemical Composition Zro2+hfo2+y2o3 | ≥99% |
| Aging Surface Monoclinic Phase Content | <15% |