SYSTEM NE is a non-precious dental cast alloy for crowns and bridges on cobalt-base, type 4.
SYSTEM NE is easy to use and quick to polish with excellent laser welding properties.
The alloy can be melted by open flame or induction heating.
SYSTEM NE can be used with any commercial, phosphate-bonded investment material (our recommendation: ADENTA®-VEST CB).
SYSTEM NE can be veneered with any high-fusing ceramics.
Typical material properties
| Property | Value |
|---|---|
| Yield strength 0,2 % (MPa) | 500 |
| Elongation (%) | 9,0 |
| E-module (GPa) | 210 |
| Tensile strength (MPa) | 720 |
| Density (g/cm³) | 8,4 |
| CTE (25 – 500°C) (10⁻⁶ K⁻¹) | ~ 14,2 |
| Hardness HV 10/30 | 300 |
| Delivery form (mm) | Ø 9,5 x 11 |
| Packaging unit (g) | 1000 |
| Type acc. DIN EN ISO 22674 | Type 4 as delivered |
Lot numbers may show minimum deviation from typical values. More information are available on our instruction for use.
Chemical composition %
| Element | % |
|---|---|
| Co | 64,4 |
| Cr | 21 |
| Mo | 6,5 |
| W | 6,4 |
| Si | 0,8 |
| Mn | 0,65 |
| Fe | 0,1 |
Free of Be, Cd and Pb. Ni < 0,1%
Informations produit
| Fabricant | Adentatec |
|---|---|
| Lead Free | Oui |
| Polishing | Quick to polish |
| Alloy Type | Cobalt-base, type 4 |
| Application | Couronnes et bridges |
| Cadmium Free | Oui |
| E Module Gpa | 210 |
| Iron Percent | 0,1 |
| Density G Cm3 | 8,4 |
| Laser Welding | Excellent laser welding properties |
| Beryllium Free | Oui |
| Cobalt Percent | 64,4 |
| Melting Method | Open flame or induction heating |
| Nickel Percent | < 0,1% |
| Silicon Percent | 0,8 |
| Veneer Material | Any high-fusing ceramics |
| Chromium Percent | 21 |
| Delivery Form Mm | Ø 9,5 x 11 |
| Packaging Unit G | 1000 |
| Tungsten Percent | 6,4 |
| Hardness Hv 10 30 | 300 |
| Manganese Percent | 0,65 |
| Elongation Percent | 9,0 |
| Molybdenum Percent | 6,5 |
| Investment Material | Any commercial, phosphate-bonded investment material (recommendation: ADENTA®-VEST CB) |
| Precious Metal Free | Non-precious |
| Cte 25 500c 10 6 K 1 | ~ 14,2 |
| Tensile Strength Mpa | 720 |
| Type Din En Iso 22674 | Type 4 as delivered |
| Yield Strength 0 2 Percent Mpa | 500 |