ZIRCONIO 3D PRO
Santa Barbara SRL · #26644 · source
Santa Barbara DentalSanta Barbara 3D Pro Multilayer Zirconiais the ideal solution to ensure the required high aesthetic standard.The layers with different colors,the high translucency and strength (from 800 to 1200 Mpa) oer a wide range of operational possibilities for the entire dental arch. Available in 16 colors and dierent thicknesses for each application necessary for personalized, safe and natural-looking restorations. Compatible with the entire Santa Barbara Dental fleet •16 Vita colors + 4 Ivoclar Bleach colors • 5 layers with increasing strength (800 Mpa; 900 Mpa; 1000 Mpa; 1100 Mpa; 1200 Mpa) • Translucency 49% - 42% • Natural tooth looking • Lightweight and durable • Biocompatible • Low thermal conductivity • Suitable for monolithic anterior restorations Chemical Composition
Components
ZrO2+HfO2+Y2O3 ≥99%
Y2O3 4.5%-10%
Al2O3 <0.15%
Other Oxides <0.05%
Physical Properties
Properties
Density before sintering (g·cm−3) 3.15 ±0.05
Density after sintering (g·cm−3) 6.07 ±0.02
CTE (25-500°C) 10.5 ±0.05
Flexural strength after sintering (Mpa) 800-1200
Aging surface monoclinic phase content <15%
Light Transmittance 42-49%
Chemical solubility after sintering (µg·cm−2) <100
Cytotoxicity Livello 0
Radioactivity (Bq·g−1) <0.1
Sintering Temperature (recommended 1500) 1480 -1530
Informations produit
| Fabricant | Santa Barbara SRL |
|---|---|
| Y2o3 | 4.5%-10% |
| Al2o3 | <0.15% |
| Poids | 440 g |
| Cytotoxicity | Livello 0 |
| Other Oxides | <0.05% |
| Colore Cialda | A1, A2, A3, A3,5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4 |
| Misure Cialde | ∅98×10, ∅98×12, ∅98×14, ∅98×16, ∅98×18, ∅98×20, ∅98×25, ∅98×22 |
| Zro2+hfo2+y2o3 | ≥99% |
| Cte (25 500°c) | 10.5 ±0.05 |
| Light Transmittance | 42-49% |
| Sintering Temperature | (recommended 1500) 1480 -1530 |
| Radioactivity (bq·g−1) | <0.1 |
| Density After Sintering (g·cm−3) | 6.07 ±0.02 |
| Density Before Sintering (g·cm−3) | 3.15 ±0.05 |
| Aging Surface Monoclinic Phase Content | <15% |
| Flexural Strength After Sintering (mpa) | 800-1200 |
| Chemical Solubility After Sintering (µg·cm−2) | <100 |